Glass magnesium board anti-halogen, you have a way to solve this problem?
Soaked in water after the product will drop the intensity of 30 to 60% range, kanban inside the effective crystal content.
You said the water droplets powerful, should be considered very serious, it is recommended to find manufacturers claims, even soaked in water, can not ensure that no again halogen, as long as there is anti-halogen situation, the surface is basically can not paint.
If you do not pursue the strength, you can soak the warm water, the water temperature of 40 to 50 or so, can effectively dissolve the excess of the CL ions in the board, so as to reduce the situation of anti-halogen. The amount of water should not be less than 4 times the volume of the product itself.
Hollow magnesium is anti-halogen, magnesium sulfide can now solve this problem of anti-halogen, bearing capacity is also very strong!