In the fastener industry, 1018 refers to what material
Simple point is the wire friends, the general is the production of screws. Rivet material is generally 1215
Low carbon steel, can only be used to produce the general screw class, and 102A almost
1018 is the United States material, you can use domestic steel instead. Processing, do, use, distribution of US bolts and nuts, US bolts and nuts, American standard bolts and nuts, must have the US screw standard. You should buy a set of the latest US fastener standards Daisy "IFI English Fastener Standard Handbook, eighth edition) (published in English) (published in 2011), experts are the winner, have the standard will have the relevant business.
Low carbon steel, generally used for the production of self-tapping screws and screws and other low-strength fasteners products. 1018 steel chemical composition percentage: carbon C: 0.17-0.24; manganese Mn: 0.7-1.0; nickel Ni <= 0.25; phosphorus P: <= 0.035; sulfur S: <= 0.035; silicon Si: 0.17-0.37; <= 0.25; copper Cu: <= 0.25 domestic commonly used 18A and 22A material, carbon 0.18%. Domestic steel mills are now used daily SWRCH18A
Low-carbon steel. Domestic in accordance with the Japanese standard to create the SWRCH18A. (JIS G 3507) Carbon C: 0.15 to 0.20 Silicon Si: 0.17 to 0.37 Mn Mn: 0.60 to 0.90 Phosphorus P: ≤0.030 Sulfur S: ≤0.035 The carbon content of the material is relatively low and can not be quenched and tempered. Used for cold piers to make low-grade screws. Pull up the strength of 450Mpa.