Question:

Want to make some drill sleeves with T10 steel?

I wonder if it works Because of the large number of drilled holes, the wear of common steel is relatively large. But T10 steel needs quenching. I don't have any specialized equipment here. Usually it is heated by oxygen acetylene, and then it is quenched by oil. I wonder if T10 steel is good. What about the deformation? Outside diameter 15mm, inner hole 8.6MMIf not, what is the best way to do it? Or what to replace?

Answer:

I analyze your accuracy requirements are not high, no problem. The heating temperature is not too high, oil cooling, then take the gun fire roast, return fire, file inspection for hardness
Tolerable。 T06 or T08 can, but should not wear very fast quenching, the inner diameter of H8, H9, such as the outer diameter with H8/n7 this can often remove.
As the drill material set is the first choice of bearing steel GCr15, the quenching temperature is 835 ~ {850 cooling medium: oil, the tempering temperature is 150 ~ 170 hardness can reach 61 ~ 65}, GCr15 bearing steel with good hardenability, high abrasion resistance, high fatigue life. In general industry, this material is commonly used as drill sleeves. Carbon tool steel T10 drill can also set {the quenching temperature is 780 cooling medium: water or oil, the tempering temperature is 200 ~ 250 hardness of 60 ~ 64} in the use of performance is far better than GCr15 bearing steel. If there is no professional heat treatment equipment should pay attention to the quenching temperature and tempering temperature, especially the quenching temperature is 835 ~ 850 and I hope to help you.