What are the elements of the national standard aluminum rod 6063t5?
chemical compositionAluminum Al: marginSilicon Si:0.20 ~ 0.60Copper Cu:0.10Magnesium Mg:0.45 ~ 0.9Zinc Zn:0.10Manganese Mn:0.10Titanium Ti:0.10Chromium Cr:0.10Iron Fe:0.35Single: 0.05 total: 0.15
The method is available through water or water quenching of the thin-walled parts (6<3mm. You can also implement the wind quenching).Good weldability and corrosion resistance, no tendency to stress corrosion cracking. Al-Mg-Si alloy is the only alloy that has not found stress corrosion cracking in heat treated reinforced aluminum alloyAfter processing, the surface is very smooth and easy to anodizing and coloring. Its disadvantage is that if it is stayed at room temperature for a period of time after quenching, it will have an adverse effect on the strength (parking effect)
6063 aluminum rod is a low alloying Al-Mg-Si system high plasticity alloyHas many valuable characteristics:Heat treatment strengthening, high impact toughness, is not sensitive to defectsHave excellent thermoplastic, can be squeezed into a high-speed complex structure. The hollow thin wall. Various profiles or forged into the complex structure of the forging, quenching temperature range, the quenching sensitivity is low, extrusion and forging after stripping, as long as the temperature is higher than the quenching temperature.