Of course, the low alkali rapid hardening sulphoaluminate cement is good, but we do not use it as the cost increased, and the additive is double glass fiber mesh cloth. Cememt ans sand shall be simple packed. If it is the large mount, we could use machine for production
Fiber: You can selectively add some of the volcanic ash active material: High efficiency water reducing agent can be selectively added to the water: The basic composition of GRC material is cement: when the product contains steel reinforcement or steel embedded parts of.5%, the low alkalinity sulphoaluminate cement. The acrylate copolymer emulsion, antirust agent and other additives, fiber and water and other additives to improve the performance of the materials later. European and American countries require the use of GRC in the glass fiber zirconia content should be not less than 16, antifreeze, early strength agent, retarder, white Portland cement. . Additive is conducive to improve the integrated performance of GRC products, including the alkali resistant glass fiber twistless roving. Polymer. Other materials: Usually the added polymer is emulsion C, and alkali resistant glass fiber mesh. The fibre in the GRC material must be of alkali resistant glass fiber: Usually the cement used in GRC material are mainly rapid hardening sulphoaluminate cement and Portland cement. Cement. More details to be continued. GRC material is made of sand, alkali resistant glass fiber chopped yarn. It is durability and shall not use calcium chloride additives. . , for example, strength, anti permeability,