Application characteristics of high alumina brick
Reheating line change. If the firing temperature of high alumina brick products is enough and the firing time is enough, the volume is stable, the change of the reheating line is small; on the contrary, the residual shrinkage of clay brick products is caused by recrystallization.
Refractoriness. High alumina brick products are advanced varieties of aluminium silicate refractory products, and their refractoriness increases with the increase of Al2O3 content, generally not less than 1750 - 1790 DEG C. If the content of Al2O3 is more than 95% of corundum brick, the refractoriness can be as high as 1900-2000 degrees.
Thermal shock stability. In high alumina brick products, the stress concentration is due to differential expansion when the temperature of refractory brick changes. Therefore, the high aluminum brick products than clay brick products thermal shock stability is poor, general water temperature only 3 - 5 times.
Slag resistance. Due to the high alumina brick products in the three oxidation of two aluminum is neutral and high content, so this material products for acid-base slag corrosion resistance.
Load softening temperature. The softening temperature of high alumina brick products decreases with the increase of silica and alkali metal oxide content, but is higher than that of clay brick products, which is about 1420 - 1530 degrees centigrade. Al2O3. The softening temperature of corundum brick with content greater than 95% can reach above 1600 DEG C.