How many degrees does the ceramic filter melt?
Spinel is basically over 1600-1700. It's not too acid proof.There are other materials such as silicon nitride. Ceramics can be more than 1300 degrees in temperature. So the material you are using now is unlikely to melt and melt, and you can change it into one of the top materials. Baidu, this stuff is all over the street.
Alumina made from tabular corundum can be used over 1800 degrees!SiC if there is atmosphere, protection will be higher, there is no atmosphere protection, because the existence of oxidation, generally not more than 1600.Corundum, mullite, 1750 degrees small meaning.
You should say clearly what ceramic you useHowever, as a melting furnace or filter medium, alumina products are the most versatile, but also silicon carbide, corundum, mullite, spinel and so on. They use very high temperatures.