Magnesite brick and electric arc furnace melting magnesium chromium material by direct casting (see Figure microstructure, color), fused magnesia chrome brick material produced by the process of melting particles combined with magnesia chrome brick etc..
The fine powder compacts after calcination produced by magnesia - chrome ore grinding method, brick with magnesia coarse particles, are effective measures to eliminate the effect of loose. Compared with the common magnesia chrome brick, the magnesia chrome brick made by this method has lower porosity, higher compressive strength, higher softening temperature and higher flexural strength. Compacts with chrome magnesite powder, magnesia chrome brick by synthetic magnesia chrome sand made of high-temperature calcination, slag resistance and high temperature strength are better than other magnesite chrome brick.
Magnesia chrome brick to Magnesium Oxide (MgO) and chromium oxide (Cr2O3) as the main ingredient, refractory periclase and spinel as main mineral components of products. The bricks have high refractoriness, high temperature strength, strong resistance to alkaline slag, good thermal stability, and certain adaptability to acid slag. The main raw materials for making magnesia chrome bricks are sintered magnesia and chromite. The purity of magnesia raw materials should be as high as possible, chrome iron ore chemical composition requirements: Cr2O3:30 - 45%, CaO = 1 ~ 1.5%.