Welding imported aluminum AL6061-T6, what wire to use, in order to ensure that after chemical cleaning will not be chromatic aberration?.
With 4047 aluminum, temperature of 600 degrees, 4047 copper aluminum welding temperature 450-500
Using non welding metal sewing process, no stress, no deformation, no leakage, permanent repair, we have repaired the cylinder block of the cast aluminum engine, the cylinder head cracks. The main reason is that the cost is a little high, so your import must be very valuable.
The microstructure and properties of double pulsed MIG welding seam of 6061-T6 sheet aluminum alloy were studied by using ER4043 welding wire and ER5356 welding wire. The results show that the ER5356 welding wire, 6061-T6 Aluminum Alloy joint yield, tensile strength and elongation are higher than that of ER4043 welding wire as welded joint filling, welding coefficient of the former is 0.72, while the latter is only 0.65; the two joints are welding hardness of welding seam center approximate symmetrical distribution, the lowest value appeared in the area of joint thermal quenching effect of ER5356 welding wire welding joint, hardness is ER4043 high with ER5356 welding wire; weld wire as filler, 6061-T6 Aluminum Alloy as cast microstructure of fine dendrite, relatively thin, with ER4043 welding wire welding, weld cast structure of thick, and branches the crystal is developed, near the joint side fusion zone between the columnar crystal, near the heat affected zone on the side of fine equiaxed grains. Compared with the original base metal, the grain of the heat affected zone has a certain degree of coarsening. Although both of them have a small amount of two phases in the quenching area, the two of the quenching zone is smaller and diffused than that of the quenching zone when the ER5356 wire is used as filler.