What kind of refractory bricks material is best?
1, high alumina brick: The content of Al2O3 is more than 75. The refractoriness is higher than the clay brick. It has good resistance to acid, alkali and erosion and is suitable for cement kiln calcining zone and other places. It has long operation life, but the price is high. 2. dolomite?brick: Formation of coating has good performance, good corrosion resistance, but f-CaO is contained in bricks. It is hydratable and difficult to transport and keep, so it is less used in the production. 3. magnesia-chrome bricks: It has good formation of coating and is used for burning zone. The disadvantage is poor thermal shock resistant performance. Besides, positive Hexavalent Cr is highly toxic. Countries that produce and use magnesia-chrome bricks gradually decrease on the international. Now production units using this brick should find alternatives as soon as possible. 4. spinel brick: It is often used in transitional zone and has good seismic performance, good reduction resistance, but refractoriness is a little bit poor. 5. anti-stripping brick: This brick contains a small amount of ZrO. Martensite phase transformation happens to form thin crack during temperature-rise period. It has strong alkali?resistance, anti-stripping performance and good slag resistance. 6. phosphate brick: It has low refractoriness, but it has strong strength and good shock resistance. It is often used in grate?cooler, hot kiln hood, etc. 7. carborundum brick: It has high temperature resistance(1800 degree, softening temperature under a fixed load is 1620-1640), small coefficient of thermal expansion, high cold-resistance heat-resistance, abrasion resistance. It is suitable for cooling zone and kilneye. 8. silmo brick: It has good thermal shock resistance, high strength, good abrasion resistance, and is suitable for transitional belt.
Domestic experimental electric furnace body is made up of hearth, insulating layer and shell. Sic and high-alumina material are often used in traditional electric furnace under 1300℃ traditional furnace, while corundum material is used in 1600℃. Laboratory furnace of Occident usually uses ceramic fiber tank which is characterized by rapid temperature raising, good accuracy, light weight and small volume. In recent years, domestic Hangzhou blue sky Instrument and Shanghai laboratory equipment all have been produced by experimental furnace with ceramic fiber tank.
It depends on your purposes. In general, aluminous fireclay brick is usually used. GB/T 3994-2005 insulating fireclay brick. Bricks with good textile are as follows: high-grade thermal insulation refractory brick, GB/T 3995-2006 high alumina thermal insulation refractory brick. Model is A13, and the texture is aluminium oxide. A13 50u, high grade heat insulating brick B5; intermediate heat insulating brick B2, etc.
It depends on your purposes. In general, aluminous fireclay brick is usually used. GB/T 3994-2005 insulating fireclay brick. Bricks with good material are as follows: high-grade thermal insulation refractory brick, GB/T 3995-2006 high alumina thermal insulation refractory brick. Model is A13, and the texture is aluminium oxide. A13 50u, high grade heat insulating brick B5; intermediate heat insulating brick B2, etc.
In general, aluminous fireclay brick is used. GB / T 3994-2005 insulating fireclay brick. Bricks with good material are as follows: high-grade thermal insulation refractory brick, GB/T 3995-2006 high alumina thermal insulation refractory brick. Model is A13, and the texture is aluminium oxide. A13 50u, high grade heat insulating brick B5; intermediate heat insulating brick B2, etc.