What is the relationship between the two? Or who is engaged in the electronics industry, can give me talk about the industry's industrial chain and technical process? Thank you.
The concept of glass is generally hard and fragile objects, and is not suitable as a structural material, but if it is made of silk, its strength is greatly increased and has a softness, so with the shape of the resin can finally become a good structural material. Glass fiber with its diameter smaller its strength increased. As a reinforcing fiber glass fiber has the following characteristics, these features make the use of glass fiber far more than other types of fiber to a wide range of development speed is also far ahead of its characteristics are listed below:
?? (1) high tensile strength, elongation is small (3%).
?? (2) high elasticity coefficient, good rigidity.
?? (3) elastic limit within the large elongation and high tensile strength, so the absorption of large impact energy.
?? (4) for the inorganic fiber, with non-flammable, good chemical resistance.
?? (5) water absorption is small.
?? (6) scale stability, heat resistance are good.
?? (7) good processing, can be made into stocks, beams, carpets, weaving, and other different forms of products.
?? (8) transparent through the light.
?? (9) with a resin having a good adhesion to the surface treatment agent.
?? (10) cheap.
The characteristics of glass fiber
?? The concept of glass is generally hard and fragile objects, and is not suitable as a structural material, but if it is made of silk, its strength is greatly increased and has a softness, so with the shape of the resin can finally become a good structural material. Glass fiber with its diameter smaller its strength increased. As a reinforcing fiber glass fiber has the following characteristics, these features make the use of glass fiber far more than other types of fiber to a wide range of development speed is also far ahead of its characteristics are listed below:
Glass fiber is an excellent inorganic nonmetallic material. English formerly known as: glass fiber or fiberglass. Ingredients are silica, alumina, calcium oxide, boron oxide, magnesium oxide, sodium oxide and the like. It is a glass ball or waste glass as raw material by high temperature melting, drawing, yarn, weaving and other technology. And finally the formation of various types of products, glass fiber monofilament diameter from a few microns to twenty meters a few microns, equivalent to a hair of 1 / 20-1 / 5, each bundle of fiber raw silk has hundreds or even Thousands of single-wire composition, usually as a composite material in the reinforcement materials, electrical insulation materials and insulation materials, circuit boards, widely used in various areas of the national economy.