The specific grade of steel can cause the yield strength of steel round bars to vary. Here are some common yield strengths for different grades of steel round bars:
- Mild steel round bars usually have a yield strength of approximately 250 MPa (megapascals) or 36,000 psi (pounds per square inch).
- The yield strength of carbon steel round bars can range from 350 to 550 MPa or 50,000 to 80,000 psi.
- Compared to mild or carbon steel, alloy steel round bars such as 4140 or 4340 generally have higher yield strengths. The yield strength of these alloys can vary from 550 to 850 MPa or 80,000 to 120,000 psi.
- Stainless steel round bars are available in different grades, and their yield strengths can vary accordingly. For instance, austenitic stainless steels like 304 or 316 usually have yield strengths ranging from 200 to 300 MPa or 29,000 to 43,000 psi. Conversely, duplex stainless steels like 2205 or 2507 can have higher yield strengths of 450 to 650 MPa or 65,000 to 95,000 psi.
It is important to keep in mind that these values are typical ranges, and the actual yield strength of a specific grade of steel round bar may differ due to factors such as heat treatment, manufacturing process, and other variables. Therefore, it is always advisable to consult the manufacturer's specifications or industry standards for accurate and precise yield strength values of steel round bars.
The yield strength of steel round bars can vary depending on the specific grade of steel. Here are some typical yield strengths for different grades of steel round bars:
- Mild steel round bars typically have a yield strength of around 250 MPa (megapascals) or 36,000 psi (pounds per square inch).
- Carbon steel round bars can have a yield strength ranging from 350 to 550 MPa or 50,000 to 80,000 psi.
- Alloy steel round bars, such as 4140 or 4340, generally have higher yield strengths compared to mild or carbon steel. The yield strength of these alloys can range from 550 to 850 MPa or 80,000 to 120,000 psi.
- Stainless steel round bars come in various grades, and their yield strengths can vary accordingly. For example, austenitic stainless steels like 304 or 316 typically have yield strengths ranging from 200 to 300 MPa or 29,000 to 43,000 psi. On the other hand, duplex stainless steels like 2205 or 2507 can have higher yield strengths ranging from 450 to 650 MPa or 65,000 to 95,000 psi.
It is important to note that these values are just typical ranges, and the actual yield strength of a specific grade of steel round bar may differ based on factors such as heat treatment, manufacturing process, and other variables. Therefore, it is always recommended to consult the manufacturer's specifications or industry standards for accurate and precise yield strength values of steel round bars.
The typical yield strengths of different grades of steel round bars can vary greatly depending on the specific grade and its intended application. However, common grades such as A36, A572, and A514 typically have yield strengths ranging from 36,000 to 100,000 pounds per square inch (psi).