What is the difference between E4315 welding rod and E5016 electrode?
The main difference between E4315 welding rod and E5016 electrode is that E5016 welding rod is more expensive.E4315: the tensile strength of deposited metal is not less than 420MPa. It is suitable for all position welding, low hydrogen and sodium type, and direct current reverse connection;E5016: the tensile strength of deposited metal is not less than 490MPa. It is suitable for all position welding, low hydrogen and potassium type, AC or DC reverse connection.The chemical composition of both is ordinary low carbon steel, E5016 can be used instead of E4315.
Minimum tensile strength E4315 E5016 deposited metal post: 43kgf/mm^2 50kgf/mm^2 third digit (1) represents all position welding (Ping, Li, Yang, Wang) all position welding (Ping, Li, Yang, Wang) third, fourth digits: coating: (15) low hydrogen sodium (16) low hydrogen K type third, fourth digits: welding current type: reverse DC AC or DC reverse connection for reference!
Electrode type, complex, dynamic load plate structure adopted steel general structure of electrode arc welding of low carbon steel sheet, boiler pressure container, electrode type low temperature welding the welding conditions of Q235E4313, E4303, E4301, E4320, E4311E4316, E4315 (E5016, E5015) general Q255 without preheating is generally not preheated Q275E4316, E4315E5016. E5015 plate structure for preheating temperature is above 150 in 08, 10, 15, 20E4303, E4301, E4320, E4311E4316, E4315 (E5016, E5015) is generally not preheat 25E4316, E4315E5016, E5015 plate structure for preheating temperature is above 150 20g, 22gE4303, E4301E4316, E4315 (E5016, E5015) plate structure preheating 100 ~ 150 DEG 20RE4303, E4301E4316. E4315 (E5016, E5015) is generally not preheating important structure requirements for plasticity, toughness and crack resistance is high, the use of low hydrogen type E4315 (J427) or E50 15 (J507) welding rod. When using AC welding machine, AC and DC can be used, low hydrogen type E4316 (J426) or E5016 (J506) welding rod. The difference between the two is that the former is suitable for direct current and the latter for direct and direct use.